ABSTRACT The present work reports the ascorbic acid effect (0,60-0,98 µM) on the aspect ratio (AR) of gold nanorods with bands of longitudinal plasmon (LP) in the near infrared (958 -1085 nm), grown by seed-mediated chemical route. Cloroauric acid-1mM as precursor agent was used, obtained from a stock solution prepared by dissolving metallic gold (99,99%) in aqua regia. Benzyldimethylhexadecylammonium chloride (BDAC) and cetyltrimethylammonium bromide (CTAB) at molar ratio 0,75 (BDAC/CTAB) as surfactants were used. Scanning electron microscopy images implemented with a transmitted electron detector and absorption spectra revealed that the AR reaches a maximum of 7,3 and a band of PL of 1085 nm for a critical concentration of ascorbic acid of 0,68 µM, equivalent to a molar AA/Au3+ of 1,5. As ascorbic acid increase to 0,98 µM, the AR decreases up to 6 and consequently, its PL band decreases up to 958 nm.
RESUMEN El presente trabajo reporta el efecto de la concentración (0,60-0,98 µM) de ácido ascórbico sobre la razón de aspecto (RA) de nanorods de oro con bandas de plasmón longitudinal (PL) en el infrarrojo cercano (958 – 1085 nm), crecidos por ruta química mediado por semillas. Como agente precursor se usó ácido cloroáurico tri-hidratado (HAuCl4.3H2O) obtenido a partir de oro metálico de alta pureza (99.99%) disuelto agua regia. Como agentes surfactantes fueron utilizados cloruro de bencildimetilhexadecilamonio (BDAC) y bromuro de cetiltrimetilamonio (CTAB) a una razón molar de 0,75 (BDAC/CTAB). Imágenes por microscopia electrónica de barrido implementado con un detector de electrones transmitidos y los espectros de absorción, revelaron que la RA se alcanza un máximo de 7,3 y una banda de PL de 1085 nm para una concentración crítica de ácido ascórbico de 0,75 µM, equivalente a una razón molar de AA/Au3+ de 1,5. Mayor incremento de ácido ascórbico hasta 0,98 µM, la RA disminuye hasta 6 y consecuentemente, su banda de PL disminuye hasta 958 nm.